Google+ Titanium - Fabrication and use of Titanium Alloys - Manufacturing in China Blog Google+
image image image image image image
Our Mission is to support businesses in Australia through our expertise in Manufacturing in China. 
We deliver value-added services that enable companies to manage, improve, and grow their businesses.
Sheet metal work

We offer the complete sheetmetal manufacturing solution, from single part or sub-assembly to turnkey solutions for mechanical and electrical assemblies. With years of manufacturing experience, we have developed an expertise that deliver the finest quality and service.
Transformers

P&A has the expertise and facilities to custom manufacture a full range of transformers and toroids to your specification. We can design and deliver transformers to your requirements. Take advantage of our expertise and competitive pricing from China.
Aluminium diecasting

P&A offer a range of aluminium die casting services to suit clients needs predominately working with high quality aluminum enclosures and components. The fact that we are China based company enables us to deliver aluminum parts and components at most competitive pricing.
PCB

Our PCBA-based product manufacturing handles a wide range of assemblies, from single PCB assemblies to PCBAs integrated into enclosures. We support high and low PCBs for volumes and cover the entire life cycle of electronic products – from development and introduction, through to growth and maturity and end-of-life phases.
Heatsink

We designed and manufacture a wide variety of thermal solutions for various applications. Our products include U-type heat sinks, extruded heat sinks, cold forged heat sinks, stacked and folded fin heat sinks, heat pipes and heat pipe integrated solutions, TEC's, conduction cooling solutions and more.

Manufacturing in China Blog

Here you can leave comments and start discussions about manufacturing parts of complete products in China.

Titanium - Fabrication and use of Titanium Alloys

Posted by P&A International
P&A International
P&A International is China based company formed by partners with engineering background in 2008. Our main focu...
User is currently offline
on Tuesday, 30 April 2013 in General Talk

Titanium part manufactured in ChinaP&A International is a leading Supplier & Distributor of Titanium Alloy and other Titanium Products. Through designing,machining, surface finishing, fabricating & other value-added processes, we are able to manufacture titanium products to your specific needs. As well as we can supply the titanium & titanium alloys from our existing product ranges for your applications.

About Titanium

1. Corrosion Resistance

Titanium is a material with excellent corrosion resistance. It is able to withstand attack by acids, chlorine elements in water and fluorine and its compounds. Titanium actually forms a passive oxide layer when it comes into contact with any oxygen a property which serves to enhance its corrosion resistance even further. It is thus understandable why such a material would be desired in such oxygen rich environments as the human body.

2. High Strength

Titanium is an extremely strong material. Its strength matches that of common low grade steel alloys and as a result titanium is extensively used in aerospace and industrial applications.

3. High Strength- to-Weight Ratio

This is the property which separates Titanium from other high strength materials such as Steel. Titanium has the amazing property of being very high strength whilst also being very light. Without labouring too much over the physics behind this phenomenon this is simply due to the low density nature of Titanium materials.

5. Biocompatibility

Important property to mention in this article is that the human body LIKES titanium. When inserting materials into the body it is vital to choose a material which can be fully integrated into the body. So far research has shown Titanium to be the only material able to undergo this process of osseointegration. Titanium implants heal with the jaw until they become part of the jaw itself with all the same elements you would expect from a functioning body part including links to the bodies nervous and circulation systems. This integration means that titanium dental implants are not just there to improve your mouth’s aesthetics or to act as a structural bridge – what titanium provides is the ability to recreate a fully functioning tooth and therein lies the beauty of this amazing material.

 


 

Are you looking for supplier of Titanium in China? Contact Us!

titanium supplier china

 


 

Fabrication of Titanium and Titanium Alloys

Titanium and its alloys can be readily hot worked at temperatures generally somewhat lower than those used for steels. Techniques for press and hammer forging of titanium are essentially the same as for low-alloy steels. Good handling methods and plant layout will reduce the number of reheats necessary, minimizing contamination during forging.

Hot Working

Titanium and its alloys can be readily hot worked at temperatures generally somewhat lower than those used for steels. To minimize surface contamination, titanium should be held at high temperatures for only a short time before forging. The rate of contamination, relatively low up to 700°C, increases rapidly with increase of temperature.

All forging furnace atmospheres contain free or combined oxygen, and some absorption of this element inevitably occurs. In addition to visible scaling, diffusion of oxygen results in hardening of a relatively shallow underlying layer. The effect of nitrogen is not usually significant at preheating temperatures. Subsequent operations such as machining will remove the hardened surface layer, and the final product will have hardness similar to forging stock.

Hydrogen, however, diffuses more rapidly than oxygen and may penetrate the full section of the work piece, which can have a serious effect on properties. Such material can only be recovered by prolonged vacuum annealing. Hydrogen is absorbed from both reducing and oxidizing gas- and oil-fired furnaces, but at a tolerably slow rate under strongly oxidizing conditions.

The order of preference of preheating atmospheres is therefore dried air (electric heating), undried air (electric heating), oxidizing oil- or gas-fired furnaces. Direct flame impingement must be avoided.

Forging. Techniques for press and hammer forging of titanium are essentially the same as for low-alloy steels. Good handling methods and plant layout will reduce the number of reheats necessary, minimizing contamination during forging. Because of the rapid cooling and the fairly narrow hot working range, the chilling effect of tools should be reduced to a minimum by keeping contact time as short as possible. Preheating the tools also helps. Repeated light blows, or attempts to continue forging at too low a temperature, may promote internal cracking and should be avoided. Moreover, a large number of reheats with only a small amount of deformation between heats is also detrimental, because it leads to a coarsening of the microstructure and consequently poor mechanical properties.

In drop forging, die contours should have larger radii and fillets than those used for steel; the lower thermal contraction of titanium requires a smaller shrinkage allowance. Trimming should be carried out hot; furnace, drop hammer and trimming press should be as close together as possible to minimize preheating and avoid wasting time and heat. A final stress-relief anneal is recommended.

Forming

Annealed and solution treated sheet can be pressed, stretch-formed, spun and dimpled, but maximum deformation depends upon the load being applied slowly. Good results are achieved with hydraulic presses, the rubber-pad method being useful for forming light-gauge parts. Drop hammer forming, with heated blanks, is widely used for sheet metal parts of complex contour. Punch presses, which should be slowed down to half or one-third their normal speed, can also be used.

Blanks may be prepared for forming by shearing, sawing, nibbling or blanking, using slow cutting speeds. Edge condition is important, and edge cracking may be minimized by keeping the guillotine blade sharp and close fitting or by heating metal before shearing. All burrs must be removed and, for more difficult forming operations, cut edges may need filing or polishing.

Simple shapes can be formed at room temperature, deformation being limited by the strength and springiness of the material. Solid lubricants such as soap, molybdenum disulphide or graphite are preferred to mineral oils and greases. ICI "Trilac" coating and polythene sheeting have been found to effect considerable improvement in difficult pressing operations.

For more complicated designs, the work piece and, where possible, the dies should be heated to facilitate forming. The use of heat in forming increases ductility, which is reflected in lower minimum bend radii and reduces both the load required to effect deformation and subsequent spring-back, thus ensuring greater accuracy.

Furthermore, at elevated temperatures, the spread between yield and ultimate strengths is increased, which also aids forming. The temperature to select for hot forming depends upon the alloy and the severity of the shape to be produced. Good results can be expected using temperatures of about 200-300oC for commercially pure titanium and IMI Titanium 230, and 550-650oC for IMI Titanium 317 and 318.

 


 

Are you looking for supplier of Titanium in China? Contact Us!

titanium sheet supplier china

 


 

Heat Treatment

With heating in conventional furnaces there is always some surface contamination and a risk of hydrogen absorption. Vacuum treatment, though ideal, is rarely practicable, so it is customary to use ordinary electric furnaces; hydrogen pick-up is not usually excessive. Fuel-fired furnaces should be avoided if at all possible; titanium rapidly absorbs free or combined hydrogen from the surrounding atmosphere, and this can be serious, particularly with thin sections.

Superficial hardening by oxygen diffusion is almost inevitable at the higher annealing and preheating temperatures suggested for some titanium alloys. The hardening effect is insignificant at low annealing temperatures but above 600°C may lead to surface embrittlement. Both the oxide film and the underlying oxygen-rich layer should therefore be removed by one of the methods of surface treatment; this is particularly important for high-strength alloys.

Machining and Grinding

Titanium and its alloys can be machined successfully on conventional machine tools provided that certain requirements are satisfied. In all machining operations rigidity of both work piece and cutting tool is desirable. Best results will be obtained if the cutting tools have a good surface finish. If the cutting tools are in good condition, it is no more difficult to machine titanium than an alloy steel of equivalent strength.

Titanium has a tendency to gall or smear on to other metals. Sliding contact between the work piece and its support should be avoided, and the use of roller steadies and running centres is recommended.

Turning. In general, cutting speeds should be low and feeds as coarse as practicable. A good surface finish can be obtained with very coarse feeds by using suitably shaped tools with a large nose radius. This will, however, be limited by work piece rigidity as a large nose radius causes increased tool loads and work piece deflection. Due to the lower elastic modulus of titanium, these deflections are greater than would occur on steel workplaces.

Tool materials may be high-speed steel, cast alloy, or tungsten carbide. The "super" grades of high-speed steel are satisfactory, giving good results in turning where large feeds can be employed, and particularly where the surface is rough or the cut intermittent. Tungsten carbide may be necessary for heavy work on certain harder alloys or for intermittent cutting, but in general its use is confined to lighter, more continuous cuts. For economic use of carbide tools it is essential to regrind before wear becomes excessive, and mechanically clamped tips are an obvious advantage.

Threading. Single-point screw cutting is preferable to threading with a die. Conventional methods of screw-cutting can be used, but success can also be achieved when increments of cut of 0.25-0.50 mm are applied at right angles to the axis of the component. Cuts of less than 0.13 mm should be avoided. Machine tapping with cutting speeds up to 6 m/min is preferable to hand manipulation. Tapping of full threads should be avoided: a thread of 80% depth is much easier to tap and loses little strength.

Planing. Shaping and planing of titanium are not difficult, provided that the foregoing requirements of rigidity, speed and feed are satisfied. Tungsten carbide tools with a large radius, producing a broad and relatively thin chip, are most successful. As in all cutting operations, it is essential to use sharp tools and replace them before appreciable wear occurs. For planing, clamped circular buttons of tungsten carbide have obvious advantages.

Milling. In milling, the chief problem arises from chips welding on to the teeth, resulting in cutter chipping and breakage. This is minimized with climb milling, in which the tooth finishes its cutting stroke when moving parallel to the feed. Absolute rigidity is necessary to avoid chatter, but the chip is only attached to the tooth by a thin sliver which is easily broken off.

Drilling. Titanium may be drilled with short high-speed-steel drills; the holes should be as shallow as possible. A 140o point is best for sizes below 6-5 mm and a 90° or double-angle point for larger sizes. For holes of a depth greater than five diameters, it is helpful to retract the drill at intervals and clear the swarf. Flood lubrication with a heavily chlorinated cutting oil reduces frictional troubles.

Grinding. A reduction in wheel speed to a half or a third of the conventional speed, together with the use of a suitable coolant, will usually achieve an acceptable grinding ratio. Water-base soluble oils result in poor wheel life, but some chlorinated or sulphurised grinding oils, and solutions of vapour-phase rust inhibitors of the nitrite-amine type, are satisfactory.

Polishing. Titanium can be mechanically polished by techniques similar to those used for stainless steel; reductions in wheel or mop speeds are often beneficial. If a high polish is required, light pressures are necessary during the final operations. Good results have been obtained with a canvas wheel coated with 240E1 `Alundum` grit, which can be blended with stearic acid for a finer finish.

Descaling and Surface Treatment

When titanium and its alloys are heated in air, absorption of oxygen and, to a lesser extent, nitrogen, results in the formation of an outer layer of oxide and nitride and an underlying thin layer into which oxygen and nitrogen have diffused. Removal of this hardened metal layer is essential for optimum mechanical properties, and an integral part of any descaling process.

All types of scale can be removed in fused caustic soda, but use of an unmodified bath leads to hydrogen contamination and poor surface quality. The sodium hydride process results in good surfaces and efficient scale removal but, again, hydrogen contamination occurs. Consequently, neither process is suitable for thin sections.

Caustic soda with about 10% oxidizing additions can be used for slightly thicker material, descaling conditions being 20-30 minutes immersion (longer for very heavy scale) at 425°C. Reaction between titanium and any fused caustic soda bath may lead to a dangerous build-up of heat if a stack of thin sheet is descaled. Thin-gauge material should, therefore, be handled in small batches, at a temperature not exceeding 425°C.

Anti-galling Treatments. The tendency for titanium to gall when in sliding contact with itself or with other materials can be reduced by some form of surface treatment. This is particularly desirable for bearing surfaces and for threads of bolts. Both anodizing and `Sulfinuz` treatments reduce the galling tendency, while adherent nickel and chromium deposits provide good wear resistant surfaces. Cadmium plating or the use of anti-galling paints are effective in preventing seizure of bolt threads. Details of electro deposition and anodizing procedures are given in the following paragraphs.

Electrodeposition. Adherent metallic coatings can only be electrodeposited on to titanium if the surface is suitably prepared. A procedure which has been found successful for depositing nickel, chromium, zinc and cadmium on to some titanium alloys uses a pretreatment comprising: (1) Vapour degrease, (2) Hydrochloric acid etch, 5 min in concentrated HCl at 90-110°C, (3) Cold water rinse, (4) Nickel strike for 3 min, (5) Cold water rinse.

Anodizing. Surface properties of titanium and its alloys can be modified by anodic oxidation treatment, which covers the entire surface with a thin but compact oxide film. Almost any aqueous solution can be used, but immersion in a solution of 80% phosphoric acid, 10% sulphuric acid and 10% water gives a particularly coherent film. A potential increasing from 0 to 110 volts over ten minutes should be applied.

Anodized titanium has no affinity for dyestuffs, but the film itself shows interference colors, determined by the final anodizing potential.

 


 

Are you looking for supplier of Titanium in China? Contact Us!

custom titanium parts made in China

0 votes
P&A International is China based company formed by partners with engineering background in 2008. Our main focus is manufacturing of skill and technology intense parts and components in China. Been a small player in the market we work very hard to establish ourselves by providing our clients personalised service, often going outside of our scope to support them.

Comments

P&A International
P&A International
P&A International is China based company formed by partners with engineering background in 2008. Our main focu...
User is currently offline
P&A International Monday, 28 October 2013

More general information about Titanium can be also found at Wikipedia page: http://en.wikipedia.org/wiki/Titanium

Please login first in order for you to submit comments
Contact NOW
+8615999826734
SKYPE: paddyzou123124
PREFER MSN?
paddyzou123@hotmail.com
...
Subscribe to RSS feeds, visit our Google+ page, follow us on Twitter, Facebook or LinkedIn or read the Manufacturing in China blog.